Innovation of pig iron making technology rapidly to produce high pure pig iron under low temperature and high oxygen potential by microwave irradiation
| Project Area | Microwave-Excited, High-Temperature Thermally Non-Equilibrium Reaction Fields |
|---|
| Project/Area Number |
18070003
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research on Priority Areas
|
| Allocation Type | Single-year Grants |
|---|
| Review Section |
Science and Engineering
|
|---|
| Research Institution | Tokyo Institute of Technology |
|---|
Principal Investigator |
NAGATA Kazuhiro 東京工業大学, 大学院・理工学研究科, 教授 (70114882)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
WATANABE Takashi 東京工業大学, 大学院・理工学研究科, 助教 (70361780)
|
|---|
| Project Period (FY) |
2006 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥187,700,000 (Direct Cost: ¥187,700,000)
Fiscal Year 2010: ¥29,300,000 (Direct Cost: ¥29,300,000)
Fiscal Year 2009: ¥56,400,000 (Direct Cost: ¥56,400,000)
Fiscal Year 2008: ¥39,000,000 (Direct Cost: ¥39,000,000)
Fiscal Year 2007: ¥39,000,000 (Direct Cost: ¥39,000,000)
Fiscal Year 2006: ¥24,000,000 (Direct Cost: ¥24,000,000)
|
|---|
| Keywords | 環境技術 / 金属生産工学 / 省エネルギー / 二酸化炭素排出削減 / 反応分離工学 / 鉄鉱石 / 還元 / 銑鉄 / マイクロ波加熱 / 低温製鉄 / 炭材内装ペレット / 還元速度 |
|---|
| Research Abstract |
Molten pig iron with about 3 mass% was produced from mixed powder of magnetite and graphite during about 10 min by means of microwave heating with 2.45 GHz. The concentrations of impurities in pig iron were very low and especially that of phosphorous was one tenth in pig iron produced in blast furnace. It is realized that the refractories of reaction chamber should be cooled preventing them from absorbing microwave and melting itself and that microwave beams with weak power are concentrated to make high power zone at resources. 20kW furnace producing about 30kg of pig iron per day was successfully constructed and 120kW furnace producing 1 ton per day is now constructing.
|