| Project/Area Number |
01850154
|
|---|
| Research Category |
Grant-in-Aid for Developmental Scientific Research
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
金属加工(含鋳造)
|
|---|
| Research Institution | The university of Tokyo |
|---|
Principal Investigator |
SAKUMA Taketo Professor, University of Tokyo, 工学部, 教授 (50005500)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KIKUCHI Norihumi Mitsubishi Material Co. Ltd., 中央研究所, 室長
YOSHIZAWA Yu-ichi Research Assistant, University of Tokyo, 工学部, 助手 (00200973)
菊地 則文 三菱金属(株), 中央研究所, 室長
|
|---|
| Project Period (FY) |
1989 – 1991
|
| Project Status |
Completed (Fiscal Year 1991)
|
| Budget Amount *help |
¥10,400,000 (Direct Cost: ¥10,400,000)
Fiscal Year 1991: ¥1,300,000 (Direct Cost: ¥1,300,000)
Fiscal Year 1990: ¥1,500,000 (Direct Cost: ¥1,500,000)
Fiscal Year 1989: ¥7,600,000 (Direct Cost: ¥7,600,000)
|
|---|
| Keywords | alumina / zirconia / Al_2O_3-ZrO_2 / superplasticity / grain growth / Al_2O_3-ZrO_2 / Al_2O_3ーZrO_2(アルミナ-ジルコニア) |
|---|
| Research Abstract |
The results obtained are summarized as follows,
(1) The high-temperature deformability in TZP is improved by an addition of small amount of grain boundary glass phase. The addition of 5 wt% lithium-aluminosilicate glass results in about 200ﾟC decrease of superplastically deformed temperature. TZP containing this glass deforms superplastically at 1100ﾟC.
(2) The marked grain growth and cavitation during high-temperature deformation retards the tensile ductility of high-purity Al_2O_3. The MgO addition effectively suppresses the grain growth of Al_2O_3 and consequently improves the ductility. The maximum elongation obtained is 70% at 1400ﾟC.
(3) The high-temperature flow stress in Al_2O_3-ZrO_2 depends markedly on zirconia content. A sharp peak value is obtained in Al_2O_3-2wt%ZrO_2. The composition dependence of flow stress can qualitatively be explained by assuming that the grain boundary sliding is much difficult along Al_2O_3/ZrO_2 boundary than other boundaries.
|