Sythesis of Ultranarine from The Shirasu and Zeolites.
| Project/Area Number |
05650963
|
|---|
| Research Category |
Grant-in-Aid for General Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
資源開発工学
|
|---|
| Research Institution | Kagoshima University |
|---|
Principal Investigator |
UEMURA Hisako Kagoshima Univ.Fac.of Eng., Research Associate, 工学部, 助手 (20041535)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MURAOKA Fumiko Kagoshima Univ.Fac.of Eng., Research Assistant, 工学部, 教務職員 (90229948)
SHIMO Tetsuro Kagoshima Univ.Fac.of Eng., Associate Prof., 工学部, 助教授 (80041565)
|
|---|
| Project Period (FY) |
1993 – 1994
|
| Project Status |
Completed (Fiscal Year 1994)
|
| Budget Amount *help |
¥2,000,000 (Direct Cost: ¥2,000,000)
Fiscal Year 1994: ¥600,000 (Direct Cost: ¥600,000)
Fiscal Year 1993: ¥1,400,000 (Direct Cost: ¥1,400,000)
|
|---|
| Keywords | ULTRAMARINE / SHIRASU / P-TYPE ZEOLITE |
|---|
| Research Abstract |
Shirasu are widely distributed as accumulation of volcanic eruption over Southenrn part of Kyushu. We investigated on synthesis of Ultramarine from Shirasu, Na-P type zeolite and filtrate of Na-P by hydrothermal treament at 100-120ﾟC.
By hydrothermal treatment under controled alkarine condition, the Shirasu was early transformed to hydroxysodalite and Na-P type zeolite. As the addition of NaCl was increased, sodalite was obtained. The sodalite (3Na_2O・3Al_2O_3・6SiO_2・2NaCl), hydroxysodalite (3Na_2O・3Al_2O_3・6SiO_2・2H_2O) and Ultramarine (3Na_2O・3Al_2O_3・6SiO_2・NaS_3) have a same framework.
Therefore, Shirasu was treatmented with various Sulfurs (S,Na_2S,Na_2SO_4, Na_2S_2O_3) under various alkarine condition at 120ﾟC for insertion of Sulfur into sodalite framework.
The sodalites framework (S.S) containing Sulfur similar to Ultramarine were derived from Shirasu, Na-P type zeolite and P-filtrate with various Sulfurs. But, when a large amount of sulfur (S,Na_2S) was added, Natrodavyne (3Na_2O・3Al_2O_3・6SiO_2・Na_2CO_3) was obtained.
Blue-, red-, yellow-and white-Ultramarine were obtained when were calcinated various kind of sodalite framework S.S containing sulfur for 2-4 minute at 1250ﾟC.In conclusion, the S.S derived from Shirasu were more colorful than Na-P type zeolite and P-filtrate when calcinated for coloring. It was understanded that sulfur were contained 7.8% in S.S derived from Shirasu (8.6% in case of Ultramarine).
|