Grant-in-Aid for Scientific Research (B)
| Project/Area Number |
07455265
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Nagoya Institute of Technology |
|---|
Principal Investigator |
ABE Yoshihiro Nagoya Institute of Technology, Faculty of Engineering, Professor, 工学部, 教授 (90024223)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KASUGA Toshihiro Nagoya Institute of Technology, Faculty of Engineering, Assistant, 工学部, 助手 (30233729)
NOGAMI Masayuki Nagoya Institute of Technology, Faculty of Engineering, Professor, 工学部, 教授 (90198573)
|
|---|
| Project Period (FY) |
1995 – 1996
|
| Project Status |
Completed (Fiscal Year 1996)
|
| Budget Amount *help |
¥5,000,000 (Direct Cost: ¥5,000,000)
Fiscal Year 1996: ¥1,100,000 (Direct Cost: ¥1,100,000)
Fiscal Year 1995: ¥3,900,000 (Direct Cost: ¥3,900,000)
|
|---|
| Keywords | Porous material / Glass-ceramic / Phosphates / NASICON / Ion exchange / Bacteriostatic property / Catalyst / Titanium Phosphate |
|---|
| Research Abstract |
Microporous glass-ceramics utilizing spinodal-type phase separation in glass have great advantages over porous ceramics prepared by conventional powder-sintering methods. They have wellcontrolled continuous pores and may be obtained in a desired shape and dimension. This processing is relatively simple and crystalline phases with active function can also be precipitated as the skeleton of the porous materials. Porous glass-ceramics with a skeleton of LiTi_2 (PO_4) _3 show excellent cation exchange properties that Li^+ ions in glass-ceramics are selectively exchanged with Ag^+ ions. In the present work, porous glass-ceramics with the surface phase consisting of predominantly of AgTi_2 (PO_4) _3 crystal and the interior phase of LiTi_2 (PO_4) _3 crystal were prepared by exchange of Ag^+ ions for Li^+ ions. Exchanged Ag^+ ions were chemically stable in water. Silver-containing titanium phosphate crystalline phase in the glass-ceramics did not deteriorated even by heating at 900 ﾟC.The gla
… More
ss-ceramics showed excellent bacteriostatic properties. Next, novel porous glass-ceramics with a skeleton of CuTi_2 (PO_4) _3 or CuTi_4 (PO_4) _6 were prepared by controlled crystallization of a glass and subsequent chemical leaching of the resulting dense glass-ceramic. A volume-crystallized dense glass-ceramic composed of CuTi_2 (PO_4) _3 and Cu_3 (PO_4) _2 whose surface was covered by a CuO thin layr was prepared by reheating a glass with a nominal composition in the pseudo-binary system CuTi_4 (PO_4) _6 -Cu_3 (PO_4) _2 in air. When the resultant glass-ceramic was leached with dilute H_2SO_4, Cu_3 (PO_4) _2 and CuO phases were dissolved out selectively, leaving a crystalline CuTi_2 (PO_4) _3 skeleton. On the other hand, the HCl-leaching of the same mother glass-ceramic left a crystalline CuTi_4 (PO_4) _6 skeleton. Their specific surface areas of the porous glass-ceramics were 50-70 m^2/g. The porous glass-ceramics showed much higher activity in the conversion reaction of propene into acrolein or 2-propanol into aceton than the catalysts obtained by a conventional sintering of powdery materials. Less
|
Report
(3 results)
Research Products
(15 results)