| Project/Area Number |
07457475
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
補綴理工系歯学
|
|---|
| Research Institution | Nagasaki University |
|---|
Principal Investigator |
UDOH Koh-ichi (1996-1997) Nagasaki University Instructor School of Dentistry, 歯学部, 助手 (60145266)
安田 克廣 (1995) 長崎大学, 歯学部, 教授 (50013884)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TANAKA Yasuhiro Nagasaki University Instructor School of Dentistry, 歯学部, 助手 (10217086)
HISATSUNE Kunihiro Nagasaki University Professor School of Dentistry, 歯学部, 教授 (20037526)
有働 公一 長崎大学, 歯学部, 助手 (60145266)
|
|---|
| Project Period (FY) |
1995 – 1997
|
| Project Status |
Completed (Fiscal Year 1997)
|
| Budget Amount *help |
¥7,800,000 (Direct Cost: ¥7,800,000)
Fiscal Year 1997: ¥1,600,000 (Direct Cost: ¥1,600,000)
Fiscal Year 1996: ¥900,000 (Direct Cost: ¥900,000)
Fiscal Year 1995: ¥5,300,000 (Direct Cost: ¥5,300,000)
|
|---|
| Keywords | Gold alloy / Platinum / Dental Precious alloy / Age-hardening / Order-disorder transformation / Transmission electron microscopy / Selected area diffraction / X-ray diffraction |
|---|
| Research Abstract |
Acoherent phase diagram of the AuCu-Pt pseudobinary system was determined mainly by means of TEM bright- and dark-field imaging and selected area electron diffraction techniques according to the hypothesis of Allen and Cahn, because a coherent phase diagram gives us more effective information to predict phase transformations related to age-hardening characteristics in an alloy system than an equilibrium phase diagram.
The following phase regions were found in the present experiments ; (1) alpha_0 single-phase of fcc disordered solid solution region ; (2) AuCu I(L1_0)fct ordered single-phase region ; (3) long-period orthorhombic superstructure AuCu II(L1_<0-S>)single-phase region ; (4) alpha + AuCu I region of two coexisting phases ; (5) AuCu I + AuCu II region of two coexisting phases ; (6) alpha + AuCu I + AuCu II region of three coexisting phases.
|