Project/Area Number |
07555227
|
Research Category |
Grant-in-Aid for Scientific Research (A)
|
Allocation Type | Single-year Grants |
Section | 試験 |
Research Field |
Metal making engineering
|
Research Institution | TOKYO INSTITUTE OF TECHNOLOGY |
Principal Investigator |
NAGATA Kazuhiro Tokyo Institute of Technology, Engineering, Professor, 工学部, 教授 (70114882)
|
Co-Investigator(Kenkyū-buntansha) |
TAGUCHI Seizi Kawasaki Steel Corporation, Iron and Steel Research Laboratories, Chief, 鉄鋼研究所, 部長(研究職)
FUKUYAMA Hiroyuki Tokyo Institute of Technology, Engineering, Research Associate, 工学部, 助手 (40252259)
SUSA Masahiro Tokyo Institute of Technology, Engineering, Associate Professor, 工学部, 助教授 (90187691)
MARUYAMA Toshio Tokyo Institute of Technology, Engineering, Professor, 工学部, 教授 (20114895)
|
Project Period (FY) |
1995 – 1996
|
Project Status |
Completed (Fiscal Year 1996)
|
Budget Amount *help |
¥21,200,000 (Direct Cost: ¥21,200,000)
Fiscal Year 1996: ¥6,800,000 (Direct Cost: ¥6,800,000)
Fiscal Year 1995: ¥14,400,000 (Direct Cost: ¥14,400,000)
|
Keywords | scrap / iron / copper / zinc / tin / chlorine / oxygen |
Research Abstract |
A new technique for removing copper from iron-based scrap has been proposed. When iron-based scraps containing copper were placed in atmosphere controlled by oxygen-chloring gas mixtures, copper was chloridized to evaporate, whereas iron was oxidized to remain in the form of solid. The evaporation rate of copper chlorides was determined by the transport of chlorides across the boundary layr. Thermodynamic and kinetic consideration gave the optimal condition for removing copper, that is, the temperature of 1100K and the gas composition of O2-10%C12.
|