| Project/Area Number |
08555018
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (A)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 展開研究 |
|---|
| Research Field |
Applied physics, general
|
|---|
| Research Institution | KYOTO INSTITUTE OF TECHNOLOGY (1997)
Kyoto University (1996) |
|---|
Principal Investigator |
SARAIE Junji (1997) Kyoto Inst.Tech., Faculty of Engneering & Design, Professor, 工芸学部, 教授 (90026154)
吉本 昌広 (1996) 京都大学, 工学研究科, 講師 (20210776)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MATSUMURA Nobuo Kyoto Inst.Tech., Faculty of Engneering & Design, Research associate, 工芸学部, 助手 (60107357)
YOSHIMOTO Masahiro Kyoto Inst.Tech., Faculty of Engneering & Design, Associate professor, 工芸学部, 助教授 (20210776)
木本 恒暢 京都大学, 工学研究科, 助手 (80225078)
冬木 隆 京都大学, 工学研究科, 助教授 (10165459)
松波 弘之 京都大学, 工学研究科, 教授 (50026035)
|
|---|
| Project Period (FY) |
1996 – 1997
|
| Project Status |
Completed (Fiscal Year 1997)
|
| Budget Amount *help |
¥14,800,000 (Direct Cost: ¥14,800,000)
Fiscal Year 1997: ¥4,600,000 (Direct Cost: ¥4,600,000)
Fiscal Year 1996: ¥10,200,000 (Direct Cost: ¥10,200,000)
|
|---|
| Keywords | photoluminescence / high spatial resolution / low temperature / confocal microscope / electronic structure / piezo actuator / photoluminescence image / nano structure |
|---|
| Research Abstract |
In this project, a novel analyzer has been developed to obtain an image of photoluminescence (PL), optical properties, or optoelectronic properties with a spatial resolution close to the diffraction limit at a low temperature. The analyzer consists of an objective with a high magnification, a novel developed thermal isolation, and an anti-vibration mechamism. A sample is scanned with piezo actuators to obtain the signal image. The sample is cooled down by a cold head with liquid He. A clear reflectance image of SiO_2/Si with a microstructure was obtained at 15 K with a spatial resolution of 0.8 mum. The spatial resolution closes to the theoretical limit determined with the wavelength of the light (632nm) and the numerical aperture of the objective (NA=0.09).
GaAs_<1-x>P_x (0.2<x<0.7) was grown on a Si substrate with a GaP buffer layr by metalorganic molecular beam epitaxy. The epilayr showed a spatial fluctuation of composition x. Using spatially reesolved PL,the dependence of PL emitted from GAAs_<1-x>P_x on composition x was precisely characterized. Peaks observed in PL of GaAs_<1-x>P_x was attributed to donor-acceptor pairs related to vacancies in epilayrs based on the results of the spatially resolved PL.
The topographic analyzer enables to investigate electronic structures of micro- and nano-structure of semiconductors with a higher sensitivity than that of an optical probe microscope. The topographic analyzer will open a new approach to study semiconductor materials and devices.
|