| Project/Area Number |
08555174
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 展開研究 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Fukui National College of Technology |
|---|
Principal Investigator |
YASUMARU Naoki Fukui Natl.Coll.Tech., Department of Mechanical Engineering, Professor, 機械工学科, 教授 (90158006)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
IBE Toshio Industrial Technical Center of Fukui Prefecture, Department of New Materials Dev, 新素材開発部, 主任研究員
OKIMURA Kunio Fukui Natl.Coll.Tech., Department of Electrical and Information Engineering, Ass, 電子情報工学科, 助教授 (00194473)
|
|---|
| Project Period (FY) |
1996 – 1997
|
| Project Status |
Completed (Fiscal Year 1997)
|
| Budget Amount *help |
¥2,500,000 (Direct Cost: ¥2,500,000)
Fiscal Year 1997: ¥900,000 (Direct Cost: ¥900,000)
Fiscal Year 1996: ¥1,600,000 (Direct Cost: ¥1,600,000)
|
|---|
| Keywords | plasma treatment / nitriding / ceramic coating / suraface treatment / chromium nitride / duplex treatment |
|---|
| Research Abstract |
Austenitic type 304 stainless steel was duplex treated by ion-nitriding at about 803 K and subsequent ion-plating of Cr-N or CrNi-N.The nitride films of Cr-N or CrNi-N were deposited in the pure N_2 or N_2-H_2 mixed gas at about 2.5 Pa with a film thickness of 3-34mum. The following results are obtained.
(1) As for the Cr-N system, the phase composition was a single phase of CrN or the mixed phases of Cr_2N and Cr. As for the CrNi-N system, it was the mixed phases of Cr^<**>N and Ni. Cr^<**>N was newly obserbed Cr nitride which may contain some Ni and identified as an f.c.c.structure (a=0.37 nm).
(2) The film hardness was about Hv 1900 for Cr-N and about Hv 1000 for CrNi-N.The depositing rate of the CrNi-N film was faster than that of Cr-N,but the surface roughness was larger.
(3) The ceramic flims of CrN coated onto the pre-nitrided steel showed the best wear resistance even under a heavy load. Among the CrN films of 3,10 and 19 mum, the CrN film with a thickness of 10 mum showed the minimum wear loss and the wear loss of CrN film with a thickness of above 10 mum coated onto the untreated steel decreased nearly to that of CrN film coated onto the prenitrided steel.
(4) The cermet films of CrNi-N coated onto the untreated steels show the good wear resistance and these films coated onto the pre-nitrided steels exhibet the inferior wear resistance compared with ones coated onto the untreated steels, being contrary to the tendency of the common ceramic films like as CrN.
|