| Project/Area Number |
12305062
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (A)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
高分子構造・物性(含繊維)
|
|---|
| Research Institution | Hiroshima University |
|---|
Principal Investigator |
HIKOSAKA Masamichi Hiroshima University, Faculty of Int. Arts and Sci., Professor, 総合科学部, 教授 (60087103)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TODA Akihiko Hiroshima University, Faculty of Int. Arts and Sci., Associate Professor, 総合科学部, 助教授 (70201655)
|
|---|
| Project Period (FY) |
2000 – 2002
|
| Project Status |
Completed (Fiscal Year 2002)
|
| Budget Amount *help |
¥27,300,000 (Direct Cost: ¥24,000,000、Indirect Cost: ¥3,300,000)
Fiscal Year 2002: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
Fiscal Year 2001: ¥10,920,000 (Direct Cost: ¥8,400,000、Indirect Cost: ¥2,520,000)
Fiscal Year 2000: ¥13,000,000 (Direct Cost: ¥13,000,000)
|
|---|
| Keywords | nucleation / polymer / induction period / crystallization / nucleating agent / rubber / crystalgrowth / morpholoogy |
|---|
| Research Abstract |
Topological mechanism of the nucleation of polymers have been studied. The direct evidence was shown for the first time that nuclei have been formed during the "inducstion period = initial stage) of the nucleation by means of Small angle X-ray scattering (SAXS). The scattering intensity of the nuclei was significantly increased by adding the nucleating agents, A new mechanism of nucleation under shear flow was presented: random coiled polymer chain can be easily elongated by pinning effect by fixed "pins" or dusts in the melt, which results in formation of bundle type nuclei and so called "shish" morphology. The onset mechanism of spherultic morphology from a single lamella was also studied. Due to topological nature of long chains, accummulation of strain on the surface of a single lamella can be seen, which results in screw dislocation and branching of lamellae will start. New method to determine the reliable melting temperature of thin lamellae of polymers was established. Using this method new method of determine the equilibrium melting temperature was also establised.
|