Development of Cold Die Forging Process for Clad Gear
| Project/Area Number |
12650132
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
機械工作・生産工学
|
|---|
| Research Institution | GIFU NATIONAL COLLEGE OF TECHNOLOGY |
|---|
Principal Investigator |
KATOH Kohzoh (2001) Gifu national coUege of technology, Mechanical Eng, Prof., 教授 (40292495)
加藤 浩三 岐阜工業高等専門学校, 助教授 (40204466)
|
|---|
| Project Period (FY) |
2000 – 2001
|
| Project Status |
Completed (Fiscal Year 2001)
|
| Budget Amount *help |
¥2,200,000 (Direct Cost: ¥2,200,000)
Fiscal Year 2001: ¥1,300,000 (Direct Cost: ¥1,300,000)
Fiscal Year 2000: ¥900,000 (Direct Cost: ¥900,000)
|
|---|
| Keywords | Plastic Forming / Cold Die Forging / Divided Metal Flow / Face Pressure |
|---|
| Research Abstract |
The relief hole-type divided metal flow die forging process was adopted to fabricate the clad gear in this research. Theinfluence of the deformation condition on the surface pressure and the metal filling into the die cavity were quantitatively evaluated The purpose in the study is to obtain the optimum deformation condition from the viewpoint of reducing the surface pressure. In the experimental simulation of the die forging, an industrial pure aluminium was employed both for the inner layer material and for the outer layer material of the clad gear. The 2 step-type die forging process" and "Die forging process with mandrel" were adopted to realize the "divided metal flow state." As a result of the experiment, the following two points were clarified. (1) The filling performance of the "2 step-type" is higher by 20〜30% than that of "1 step-type" under the same pressure condition. (2) The pressure of "2 step-type die forging process" to perform the high metal filling into the die cavity is smaller than that of "Die forging process with mandrel." And the filling rate in the case of the mandrel projection height 4mm is higher than that of 2mm."
|