| Research Field |
Civil engineering materials/Construction/Construction management
|
|---|
| Research Institution | Port and Airport Research Institute, Independent Administrative Institution |
|---|
Principal Investigator |
HAMADA Hidenori Port and Airport Research Institute, Materials Division, Head, 地盤構造部・材料研究室, 室長 (70344314)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YAMAJI Toru Port and Airport Research Institute, LCM Research Center, Project Researcher, LCM研究センター, 特任研究官 (10371767)
MIYATA Yoshikazu Port and Airport Research Institute, Materials Division, Research Engineer, 研究官 (30392989)
AKIRA Yoshikazu Port and Airport Research Institute, Materials Division, Special Research Engineer, 特別研究員 (10416018)
平崎 敏史 独立行政法人 港湾空港技術研究所, 地盤・構造部・材料研究室, 特別研究員
TAREK Uddin Mohammed 独立行政法人 港湾空港技術研究所, 地盤・構造部・材料研究室, 特別研究員(シニア)
|
|---|
| Project Period (FY) |
2003 – 2004
|
| Project Status |
Completed (Fiscal Year 2004)
|
| Budget Amount *help |
¥3,200,000 (Direct Cost: ¥3,200,000)
Fiscal Year 2004: ¥1,300,000 (Direct Cost: ¥1,300,000)
Fiscal Year 2003: ¥1,900,000 (Direct Cost: ¥1,900,000)
|
|---|
| Keywords | RC structure / Steel-concrete interface / Steel corrosion / Corrosion tendency / Corrosion rate / Chloride attack / Chloride threshold value / Interface improvement |
|---|
| Research Abstract |
In this study, several series of experimental works were carried out.
From these series of experimental works, the following research results can be obtained.
(1)By fresh concrete breeding, voids are easily formulated at steel-concrete interface.
(2)Steel corrosion in concrete is greatly affected by the steel-concrete interface.
(3)As interface voids become larger, steel corrosion clearly becomes heavier.
(4)Steel corrosion in concrete initiate at the void of steel-concrete interface.
(5)As interface voids become larger, the chloride threshold value or corrosion initiation becomes smaller.
(6)By applying the cement paste on steel surface before concrete casting, voids at steel-concrete interface become very small.
|