Applied materials science/Crystal engineering
|
|---|
| Research Institution | Osaka University |
|---|
Principal Investigator |
HIRAMOTO Masahiro Osaka University, Graduate School of Engineering, Associate professor, 大学院工学研究科, 助教授 (20208854)
|
|---|
| Project Period (FY) |
2004 – 2005
|
| Project Status |
Completed (Fiscal Year 2005)
|
| Budget Amount *help |
¥3,600,000 (Direct Cost: ¥3,600,000)
Fiscal Year 2005: ¥1,300,000 (Direct Cost: ¥1,300,000)
Fiscal Year 2004: ¥2,300,000 (Direct Cost: ¥2,300,000)
|
|---|
| Keywords | Vertical junction type organic solar cells / co-deposited film / p-i-n energetic structure / conversion efficiency of 2.5% / nanostructure control / spatial separation of photogenerated carriers / large area cell / prevention of electrical shorting / 太陽光エネルギー変換効率2.5% / オーミック接合 / ドーピング技術 / 光捕集効果 / 長期安定性試験 |
|---|
| Research Abstract |
Vertical junction type organic photovoltaic cells having a pn junction formed perpendicularly to a light irradiated surface were fabricated. Short-circuit photocurrent density of 8.5 mA/cm^2 were observed under simulated solar illumination.
Three-layered organic solar cells incorporating a codeposited interlayer of fullerene and metal-free phthalocyanine, whose nanostructure was optimized by controlling the substrate temperature during coevaporation, showed a photoelectric conversion efficiency of 2.5%.
10 cm^2 area molecular photovoltaic cells have been fabricated incorporating transparent protection layer of naphthalene tetracarboxylic anhydride (NTCDA) which completely suppress electrical shorting.
|