Ultra-morphological analysis of zirconia-veneering ceramic interface
| Project/Area Number |
16K11622
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Prosthodontics/ Dental materials science and
|
|---|
| Research Institution | Tokyo Medical and Dental University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
猪越 正直 東京医科歯科大学, 大学院医歯学総合研究科, 助教 (90753715)
|
|---|
| Project Period (FY) |
2016-04-01 – 2019-03-31
|
| Project Status |
Completed (Fiscal Year 2018)
|
| Budget Amount *help |
¥3,640,000 (Direct Cost: ¥2,800,000、Indirect Cost: ¥840,000)
Fiscal Year 2018: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2017: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2016: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
|
|---|
| Keywords | ジルコニア / 陶材 / 界面 / セラミック / 表面処理 / 機械的強度 / サンドブラスト / セラミックス |
|---|
| Outline of Final Research Achievements |
The aim of this study was to clarify the zirconia-veneering ceramic interface using ultra-morphological analysis. Surface treatments (grinding, sandblasting) affected the crystal structure of zirconia. However, three surface treatment conditions (as-sintered, ground, sandblasted) resulted in comparable fracture strength of the zirconia-veneering ceramic interface. Ultra-morphological analysis revealed tight interface between zirconia and veneering ceramics.
|
| Academic Significance and Societal Importance of the Research Achievements |
本研究では、臨床上遭遇することの多い、ジルコニア・陶材間の破折の原因を究明するため、ジルコニアへの表面処理の影響と、高解像度電子顕微鏡によるジルコニア・陶材界面の解析を行った。ジルコニアに対して表面処理を行うことで、ジルコニアの結晶構造が変化することが明らかとなった。さらに、この表面処理がジルコニア・陶材間の破折強度に与える影響は認められなかったことから、ジルコニアに陶材を築盛する際、表面処理を行う必要がない可能性が示唆された。
|