Fabrication and Control of Superhierarchical Structures of Single Crystalline Conjugated Polymers
| Project/Area Number |
17067001
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research on Priority Areas
|
| Allocation Type | Single-year Grants |
|---|
| Review Section |
Science and Engineering
|
|---|
| Research Institution | Yamagata University |
|---|
Principal Investigator |
OKADA Shuji Yamagata University, 大学院・理工学研究科, 教授 (30250848)
|
|---|
| Project Period (FY) |
2005 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥29,200,000 (Direct Cost: ¥29,200,000)
Fiscal Year 2008: ¥7,300,000 (Direct Cost: ¥7,300,000)
Fiscal Year 2007: ¥7,300,000 (Direct Cost: ¥7,300,000)
Fiscal Year 2006: ¥7,300,000 (Direct Cost: ¥7,300,000)
Fiscal Year 2005: ¥7,300,000 (Direct Cost: ¥7,300,000)
|
|---|
| Keywords | 共役ポリマー / ポリジアセチレン / 固相重合 / 単結晶 / ナノ結晶 / 固有重合 |
|---|
| Research Abstract |
ブタジイン誘導体の固相重合によって得られるポリジアセチレンの光・電子特性向上を目的とした合成的研究では、固相重合性の向上、吸収の長波長化、混晶の作製、モノマーπ共役系中の共役三重結合導入位置の違いによる固相重合部位の制御などに成功した。また、ナノメートルサイズのポリジアセチレン単結晶への官能基の導入に初めて成功し、導入した官能基を手掛かりとして基板上への共有結合による固定化にも成功した。
|
Report
(5 results)
Research Products
(50 results)