Nonlinear optical responses and ultrafast switching phenomena in conjugated polymers
Project/Area Number |
17067005
|
Research Category |
Grant-in-Aid for Scientific Research on Priority Areas
|
Allocation Type | Single-year Grants |
Review Section |
Science and Engineering
|
Research Institution | Nagoya University |
Principal Investigator |
KISHIDA Hideo Nagoya University, 大学院・工学研究科, 准教授 (40311633)
|
Co-Investigator(Kenkyū-buntansha) |
岡本 博 東京大学, 大学院・新領域創成科学研究科, 教授 (40201991)
|
Co-Investigator(Renkei-kenkyūsha) |
OKAMOTO Hiroshi 東京大学, 大学院・新領域創成科学研究科, 教授 (40201991)
|
Project Period (FY) |
2005 – 2008
|
Project Status |
Completed (Fiscal Year 2008)
|
Budget Amount *help |
¥27,600,000 (Direct Cost: ¥27,600,000)
Fiscal Year 2008: ¥4,100,000 (Direct Cost: ¥4,100,000)
Fiscal Year 2007: ¥11,300,000 (Direct Cost: ¥11,300,000)
Fiscal Year 2006: ¥4,400,000 (Direct Cost: ¥4,400,000)
Fiscal Year 2005: ¥7,800,000 (Direct Cost: ¥7,800,000)
|
Keywords | 非線形光学 / 共役系高分子 / 光物性 / 光スイッチ / ポリチオフェン / 化学ドーピング / CTポリマー |
Research Abstract |
代表的な共役系高分子であるポリチオフェンの立体規則性を高めることにより、非線形感受率が増強できることを示した。また、ドナー性を有するチオフェン分子とアクセプター分子を交互に配列した交互重合電荷移動型共役系高分子において非線形性が増大することを見出した。さらに、化学ドープしたポリチオフェンにおいてポーラロン準位を利用した多重共鳴現象により非線形感受率が増大することを見出した。
|