Solidification process of largely undercooled Fe-based alloy melt by fluxing
| Project/Area Number |
17560585
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | Akita Prefectural University |
|---|
Principal Investigator |
BITOH Teruo Akita Prefectural University, システム科学技術学部, 准教授 (40315643)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MAKINO Akihiro 東北大学, 金属材料研究所, 教授 (30315642)
|
|---|
| Project Period (FY) |
2005 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,000,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2007: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2006: ¥1,100,000 (Direct Cost: ¥1,100,000)
Fiscal Year 2005: ¥600,000 (Direct Cost: ¥600,000)
|
|---|
| Keywords | 構造・機能材料 / 結晶工学 / 金属物性 / 磁性 / ナノ材料 |
|---|
| Research Abstract |
Fe基金属ガラスにB2O3 フラックス処理を施し, 不均質核生成の原因となる介在物を除去することにより, 直径7.7 mm のFe-Co-B-Si-Nb 金属ガラス大型試料の作製に成功した。またフラックス処理と銅鋳型鋳造法を組み合わせることにより, Fe-Co-B-Si-Nb 金属ガラスの軟磁気特性を向上させた。更に, フラックス処理により液相からの核生成を制御することにより, 低透磁率と低保磁力を兼備した, 金属ガラス相と結晶相の複合材料を開発した
|