Project/Area Number |
17F17721
|
Research Category |
Grant-in-Aid for JSPS Fellows
|
Allocation Type | Single-year Grants |
Section | 外国 |
Research Field |
Inorganic industrial materials
|
Research Institution | National Institute for Materials Science |
Principal Investigator |
井出 裕介 国立研究開発法人物質・材料研究機構, 国際ナノアーキテクトニクス研究拠点, 主任研究員 (40449327)
|
Co-Investigator(Kenkyū-buntansha) |
SANGIAN DANIAL 国立研究開発法人物質・材料研究機構, 国際ナノアーキテクトニクス研究拠点, 外国人特別研究員
|
Project Period (FY) |
2017-07-26 – 2019-03-31
|
Project Status |
Completed (Fiscal Year 2017)
|
Budget Amount *help |
¥2,300,000 (Direct Cost: ¥2,300,000)
Fiscal Year 2017: ¥1,200,000 (Direct Cost: ¥1,200,000)
|
Keywords | 層状ケイ酸塩 |
Outline of Annual Research Achievements |
Reversible change in basal spacing of 2D layered materials is a very essential property for fabricating actuator systems. This interesting concept of 2D layered materials is the main motivation for us to carry out further research in order to fabricate new types of actuators which can offer faster response time and require less operating voltage. Based on this background, in this JSPS project, we focused on development of a moisture-sensitive layered silicate intercalated coordination polymers. Due to synergy effects of the intercalated coodination polymers and silicate surface (covered with silanol groups), the basal spacing of this material reversibly changed upon adsorption/desorption of water molecules.
|