Development of Olympic Gel Materials
| Project/Area Number |
17K19158
|
|---|
| Research Category |
Grant-in-Aid for Challenging Research (Exploratory)
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Polymer, Organic materials, and related fields
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
Ouchi Makoto 京都大学, 工学研究科, 教授 (90394874)
|
|---|
| Project Period (FY) |
2017-06-30 – 2019-03-31
|
| Project Status |
Completed (Fiscal Year 2018)
|
| Budget Amount *help |
¥6,370,000 (Direct Cost: ¥4,900,000、Indirect Cost: ¥1,470,000)
Fiscal Year 2018: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
Fiscal Year 2017: ¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000)
|
|---|
| Keywords | 高分子合成 / 環状高分子 / カテナン / ゲル / カチオン重合 / 架橋 / 超分子 / マグネシウム / 環 / 可逆 |
|---|
| Outline of Final Research Achievements |
We have found that magnesium bromide (MgBr2), which has never been reported as a catalyst for cationic polymerization, is useful as a Lewis acid catalyst for ring expansion cationic polymerization giving cyclic polymers effectively. We focused on the high oxophilicity of magnesium bromide and studied ring-expanding cationic polymerization in the presence of crown ether as an oxygen-based cyclic molecule, but no gelation happened.
|
| Academic Significance and Societal Importance of the Research Achievements |