| Project/Area Number |
18062005
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research on Priority Areas
|
| Allocation Type | Single-year Grants |
|---|
| Review Section |
Science and Engineering
|
|---|
| Research Institution | Kyushu University |
|---|
Principal Investigator |
HORITA Zenji Kyushu University, 大学院・工学研究院, 教授 (20173643)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
UMEMOTO Minoru 豊橋技術科学大学, 工学部, 教授 (90111921)
AMEYAMA Kei 立命館大学, 理工学部, 教授 (10184243)
TODAKA Yoshikazu 豊橋技術科学大学, 工学部, 准教授 (50345956)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥84,300,000 (Direct Cost: ¥84,300,000)
Fiscal Year 2008: ¥17,400,000 (Direct Cost: ¥17,400,000)
Fiscal Year 2007: ¥17,400,000 (Direct Cost: ¥17,400,000)
Fiscal Year 2006: ¥49,500,000 (Direct Cost: ¥49,500,000)
|
|---|
| Keywords | 巨大ひずみ / 高密度格子欠陥 / 形状不変加工 / 表面強化 / クライオミリング |
|---|
| Research Abstract |
巨大ひずみの導入過程が異なるバルク材形状不変加工や表層巨大ひずみ加工,極限巨大ひずみ加工を、いろいろな条件(ひずみ量,ひずみ勾配,圧力等)のもとで加え、高密度格子欠陥組織形成に及ぼす影響を調べた。高次に精密制御制御可能な高信頼性・高品質な巨大ひずみ材料を作製し、構造特性や力学特性の多面的解析評価のために、他の計画班に供与した。巨大ひずみ加工因子と解析評価結果をもとに、超微細組織の形成メカニズムを解明した。
|