Alloy designs and microstructural control for multi-phase hydrogen permeation alloys with large resistance to hydrogen embrittlement
| Project/Area Number |
18206072
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (A)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Structural/Functional materials
|
|---|
| Research Institution | Kitami Institute of Technology |
|---|
Principal Investigator |
AOKI Kiyoshi Kitami Institute of Technology, 工学部, 教授 (70124542)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
ISHIKAWA Kazuhiro 北見工業大学, 工学部, 准教授 (10312448)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥51,090,000 (Direct Cost: ¥39,300,000、Indirect Cost: ¥11,790,000)
Fiscal Year 2008: ¥6,890,000 (Direct Cost: ¥5,300,000、Indirect Cost: ¥1,590,000)
Fiscal Year 2007: ¥7,800,000 (Direct Cost: ¥6,000,000、Indirect Cost: ¥1,800,000)
Fiscal Year 2006: ¥36,400,000 (Direct Cost: ¥28,000,000、Indirect Cost: ¥8,400,000)
|
|---|
| Keywords | 水素透過 / 組織制御 / 耐水素脆化性 / 加工性 / 固溶係数 / 拡散係数 / ジーベルツ則 / 複合化 / 共晶組織 / 金属間化合物 |
|---|
| Research Abstract |
本研究で対象としたA-BC型(A : V, Nb, Ta, B : Ti, Zr, Hf, C : Fe, Co, Ni)複相合金では、共晶と初晶の組成を結んだ線上で良好な水素透過性と耐水素脆化性が得られる。この線上ではA量の増大につれて水素透過度(Φ)は増大するものの、耐水素脆化性が低下するから、両者のバランスを取る組成の選択が重要である。Nb-TiNi合金の水素透過度(Φ)、水素固溶係数(K)、拡散係数(D)を調べ、Kが大きいことがこの合金の特徴であることを明らかにした。
|