Plasmonic nonlinear effect of metal sphere / metal rod coated with optical Kerr medium
| Project/Area Number |
18310071
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nanostructural science
|
|---|
| Research Institution | The University of Tokushima |
|---|
Principal Investigator |
FUKUI Masao The University of Tokushima, 大学院・ソシオテクノサイエンス研究部, 教授 (70035632)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
HARAGUCHI Masanobu 徳島大学, 大学院・ソシオテクノサイエンス研究部, 准教授 (20198906)
OKAMOTO Toshihiro 徳島大学, 大学院・ソシオテクノサイエンス研究部, 助教 (60274263)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥14,380,000 (Direct Cost: ¥12,400,000、Indirect Cost: ¥1,980,000)
Fiscal Year 2008: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
Fiscal Year 2007: ¥6,500,000 (Direct Cost: ¥5,000,000、Indirect Cost: ¥1,500,000)
Fiscal Year 2006: ¥5,800,000 (Direct Cost: ¥5,800,000)
|
|---|
| Keywords | 局在表面プラズモン / 局在プラズモン / 金属ナノ微粒子 / 非線形光学効果 / 光カー媒質 / FIB加工 / ナノ材料 / 光物性 |
|---|
| Research Abstract |
銀に光カー媒質の硫化カドミウムをコートした数10nm サイズの微粒子を作製し、微粒子1個の散乱光強度が入射光強度に依存して変化する非線形光学応答の実験観測に成功した。この構造に対する計算機シミュレーション手法を開発し、実験結果と比較することで非線形光学現象の起源を明らかにした。この研究結果から、光情報処理システムの小型化・省エネルギー化に必要とされるナノサイズ光変調デバイスが実現可能であることが示された。
|