| Project/Area Number |
18350113
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer/Textile materials
|
|---|
| Research Institution | Tokyo Institute of Technology |
|---|
Principal Investigator |
KIKUTANI Takeshi Tokyo Institute of Technology, 大学院・理工学研究科, 教授 (70153046)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
SHIOYA Masatoshi 東京工業大学, 大学院・理工学研究科, 教授 (10196363)
ITO Hiroshi 山形大学, 大学院・理工学研究科, 准教授 (20259807)
TAKARADA Wataru 東京工業大学, 大学院・理工学研究科, 助教 (50467031)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
ITO Hiroshi 山形大学, 大学院・理工学研究科, 准教授 (20259807)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥16,920,000 (Direct Cost: ¥15,000,000、Indirect Cost: ¥1,920,000)
Fiscal Year 2008: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
Fiscal Year 2007: ¥5,590,000 (Direct Cost: ¥4,300,000、Indirect Cost: ¥1,290,000)
Fiscal Year 2006: ¥8,600,000 (Direct Cost: ¥8,600,000)
|
|---|
| Keywords | 分子配向 / 絡み合い / 3次元複屈折 / レーザー加熱紡糸 / 二軸延伸 / ポリエーテルエステル / 弾性繊維 / 低温特性 / 逐次二軸延伸 / 緩和時間 / 超急冷紡糸 / 絡み合い点密度 / ドローレゾナンス / 面配向 / 複屈折 / 配向結晶化 / 一軸延伸 / 応力光学則 |
|---|
| Research Abstract |
本研究では、溶融成形過程における温度・応力場の制御を、特に長緩和時間を有する構造の形成や緩和挙動に注目して行い、分子差の絡み合い構造の変化に関する検討を通じた、成形品の構造・物性変化の発現機構を明らかにすることを試みた。
絡み合いの状態は、高次構造解析で確認することができないため、絡み合い制御の直接的証拠は得られないが、さまざまな間接情報、数値解析の併用により、絡み合い制御の有用性の一端を明らかにすることができた。
|