Preparation of gelation-causing segments, development of polymer tpte of gelators containing the segments and their function evaluation
Project/Area Number |
18350115
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Polymer/Textile materials
|
Research Institution | Shinshu University |
Principal Investigator |
HANABUSA Kenji Shinshu University, 大学院・総合工学系研究科, 教授 (60126696)
|
Co-Investigator(Kenkyū-buntansha) |
SUZUKI MASAHIRO 信州大学, 大学院・総合工学系研究科, 准教授 (30334915)
|
Project Period (FY) |
2006 – 2008
|
Project Status |
Completed (Fiscal Year 2008)
|
Budget Amount *help |
¥14,950,000 (Direct Cost: ¥13,300,000、Indirect Cost: ¥1,650,000)
Fiscal Year 2008: ¥3,640,000 (Direct Cost: ¥2,800,000、Indirect Cost: ¥840,000)
Fiscal Year 2007: ¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000)
Fiscal Year 2006: ¥7,800,000 (Direct Cost: ¥7,800,000)
|
Keywords | ゲル / ゲル化剤 / 物理ゲル / ポリマー / 水素結合 |
Research Abstract |
私たちがこれまで開発してきた特に強いゲル化能を示すゲル化剤の構造をもとに、官能基を有する新規なゲル化駆動セグメントを合成した。非晶性のポリマーあるいはオリゴマーとして安価な工業中間体であるポリウレタン原料の種々のポリジオールを利用した。開発したポリマー型ゲル化剤は汎用溶媒に対し良好なゲル化能を確認した。ポリマー型ゲル化剤であるので結晶化することはなく、半永久的に安定なゲルを形成した。化粧品用のゲル化剤として有用であることを実証した。
|