Application of RB ceramics prepared by use of injection molding to non-oil tribo-system
| Project/Area Number |
18360074
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
HOKKIRIGAWA Kazuo Tohoku University, 大学院・工学研究科, 教授 (60173605)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YAMAGUCHI Takeshi 東北大学, 大学院・工学研究科, 助教 (50332515)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥17,470,000 (Direct Cost: ¥14,800,000、Indirect Cost: ¥2,670,000)
Fiscal Year 2008: ¥6,370,000 (Direct Cost: ¥4,900,000、Indirect Cost: ¥1,470,000)
Fiscal Year 2007: ¥5,200,000 (Direct Cost: ¥4,000,000、Indirect Cost: ¥1,200,000)
Fiscal Year 2006: ¥5,900,000 (Direct Cost: ¥5,900,000)
|
|---|
| Keywords | RBセラミックス / 射出成形 / 摩擦 / 摩耗 / 摺動材料 / トライボロジー / 多孔質 / 無潤滑 / 真空 / ノンオイル |
|---|
| Research Abstract |
本研究では, 射出成形を用いた新しいRBセラミックス(射出成形型RBセラミックス)を製造し, 同材料の大気中無潤滑下, 水潤滑下, 真空環境下での摩擦・摩耗特性を明らかにした. その結果, 射出成形型RBセラミックスは, 大気中無潤滑下, 水潤滑下において, 幅広いすべり速度, 荷重条件下で0.2以下の低い摩擦係数, 10^(-8)mm^2/N以下の低い比摩耗量を示した. また, 大気圧環境(1×10^5Pa)から6×10^(-3)Paまでの雰囲気圧力環境において, アルミナを相手材料とすることで0.03程度の極めて低い摩擦係数を示すことが判った.
|
Report
(4 results)
Research Products
(65 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Presentation] 入院患者用安全サンダル"安全足進"の開発2006
Author(s)
村井ユリ子, 藤盛啓成, 横塚紀美子, 赤坂純逸, 庄子由美, 仲冨千端, 糸山泰人, 里見進, 中村祐次, 山口健, 堀切川一男
Organizer
医療の質・安全学会第1回学術集会
Place of Presentation
東京
Related Report
-
-
-
-
-
-
-
-
-
-
-
-
-