Study on Novel Forming Method of Micro Surface Texture on Polymer Products Utilizing Self-Organization-Like Auto-Transformation

• Project/Area Number: 18360100
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Single-year Grants
• Section: 一般
• Research Field: Thermal engineering
• Research Institution: Tokyo Institute of Technology
• Principal Investigator: SATOH Isao Tokyo Institute of Technology, 大学院・理工学研究科, 教授 (10170721)
• Co-Investigator(Kenkyū-buntansha): SAITO Takushi 東京工業大学, 大学院・理工学研究科, 助教 (20302937) ; 川口 達也 東京工業大学, 大学院・理工学研究科, 助教 (40376942)
• Project Period (FY): 2006 – 2008
• Project Status: Completed (Fiscal Year 2008)
• Budget Amount: ¥17,400,000 (Direct Cost: ¥14,700,000、Indirect Cost: ¥2,700,000); Fiscal Year 2008: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000); Fiscal Year 2007: ¥7,540,000 (Direct Cost: ¥5,800,000、Indirect Cost: ¥1,740,000); Fiscal Year 2006: ¥5,700,000 (Direct Cost: ¥5,700,000)
• Keywords: 微細表面テクスチャ / 成形 / 自己組織化 / そり変形 / 局所加熱 / 形状制御 / レーザー照射 / 急加熱・急冷却

Research Abstract

微細形状を表面に有するプラスチック成形品を型表面の形状を転写することなしに得る手法を確立することを目的に、成形途上のプラスチック表面に自発的に生じる自己組織化的変形を利用して大面積で比較的単純な形状のテクスチャを有する製品の成形法を検討した。その結果、溶融樹脂が冷却平板に接触した際のそり変形を利用することで、成形品表面に数10 μmスケールの形状を附形できること、その形状は接触線形状を制御することで制御可能なこと、レーザー等を用いて接触部近傍の温度を制御することで形状・スケールを局所的に変更できることなどが明らかとなった。

Research Products

• [Journal Article] 炭酸ガスレーザー加熱による高分子材料表面の自己組織化的構造形成の観察 (2007)
  • Author(s): 北村弘通, 斉藤卓志, 川口達也, 佐藤 勲
  • Journal Title: 成形加工'07(プラスチック成形加工学会第18回年次大会講演論文集) (掲載決定)