structure and Dynamics of Oxygen Ion Sublattice on Thermoelectric Properties of Metal Oxides
Project/Area Number |
18360318
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Inorganic materials/Physical properties
|
Research Institution | Kyushu University |
Principal Investigator |
OHTAKI Michitaka Kyushu University, 大学院・総合理工学研究院, 准教授 (50223847)
|
Project Period (FY) |
2006 – 2008
|
Project Status |
Completed (Fiscal Year 2008)
|
Budget Amount *help |
¥17,450,000 (Direct Cost: ¥15,800,000、Indirect Cost: ¥1,650,000)
Fiscal Year 2008: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
Fiscal Year 2007: ¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2006: ¥10,300,000 (Direct Cost: ¥10,300,000)
|
Keywords | 熱電変換 / 酸化物熱電材料 / 酸素欠損 / 格子熱伝導率 / 酸化亜鉛 / フォノン散乱 / 音速 / 共ドープ / 酸素欠陥 / 秩序-無秩序構造相転移 / ペロブスカイト / ブラウンミラライト |
Research Abstract |
研究成果の概要:SrCoO_3系ペロブスカイト型酸化物の酸素イオン副格子の秩序-無秩序構造相転移に伴って熱拡散率が完全に可逆的に増減することを見出した。さらに、熱拡散率の増減は主として音速の増減によるもので、予想に反してフォノンの平均自由行程はほぼ一定であることを明らかにした。酸素イオン副格子の構造相転移に伴って、金属-酸素結合の再配列や結合角のばらつきが生じ、結晶格子の非調和性が増大した結果、フォノンの群速度が低下している可能性が示唆された。
|