Preparation of superionic metastable crystals by crystallization of glass and their application to all-solid-state batteries
| Project/Area Number |
18360319
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Osaka Prefecture University |
|---|
Principal Investigator |
TATSUMISAGO Masahiro Osaka Prefecture University, 大学院・工学研究科, 教授 (50137238)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TADANAGA Kiyoharu 大阪府立大学, 大学院・工学研究科, 准教授 (90244657)
HAYASHI Akitoshi 大阪府立大学, 大学院・工学研究科, 助教 (10364027)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥18,430,000 (Direct Cost: ¥15,100,000、Indirect Cost: ¥3,330,000)
Fiscal Year 2008: ¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Fiscal Year 2007: ¥10,270,000 (Direct Cost: ¥7,900,000、Indirect Cost: ¥2,370,000)
Fiscal Year 2006: ¥4,000,000 (Direct Cost: ¥4,000,000)
|
|---|
| Keywords | 固体電解質 / 全固体電池 / リチウムイオン / ガラス / イオン伝導体 / 硫化物 / ハイブリッド / メカノケミカル法 |
|---|
| Research Abstract |
Li_2S-P_2S_5系をベースとするガラス性液体からの超イオン伝導性Li_7P_3S_<11>結晶の析出条件を検討することによって、高いリチウムイオン伝導性と広い電位窓を兼ね備えた硫化物系固体電解質材料を開発した。得られた固体電解質を用いた全固体電池について、電極-電解質界面の構築と評価を行い、全固体リチウム電池が10mA cm^<-2>の大きな電流密度で二次電池として作動することを明らかにした。
|