Modification of Hydrophobic/Hydrophobic Thermo-Elastic Block Copolymer and Application to Biomaterials
| Project/Area Number |
18500363
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Biomedical engineering/Biological material science
|
|---|
| Research Institution | Shinshu University |
|---|
Principal Investigator |
NAGURA Masanobu Shinshu University, 繊維学部, 教授 (70021178)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
OHKOSHI Yutaka 信州大学, 繊維学部, 教授 (40185236)
GOTOH Yasuo 信州大学, 繊維学部, 准教授 (60262698)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥1,930,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥330,000)
Fiscal Year 2008: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2007: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2006: ¥500,000 (Direct Cost: ¥500,000)
|
|---|
| Keywords | スチレンーブタジエンースチレンブロック共重合体 / ブタジエンラバー / 抗血栓性 / 血小板粘着性 / 全血粘着性 / ポリエチレングリコール / グラフト / SBSブロック共重合体 / 血小板粘着 / 全血試験 / PEG / 活性化 / ブタジェンラバー / SEM / ミクロ相分離構造 / 表面 / 水酸基 / 親水性 / 疎水性 / 血小板 |
|---|
| Research Abstract |
セッ氏百数十度程度まで加熱することにより軟化し, いろいろな形状に成形できるプラスチックであるスチレンーブタジエンースチレンブロック共重合体の表面は水に親和性のない二つの微細な相に分離している. このうちブタジエン相表面のみに分子量の低いポリエチレングリコールを結合させ親水性に改質した. この表面に関し、血栓の原因となる各種血液成分の粘着実験を行ったところ, 血栓をほとんど形成しない表面を持つことがわかり、各種形状の抗血栓性材料の創製の可能性を明らかにした.
|