Characterization of glass transition dynamics of polymer nanocapsules
| Project/Area Number |
18550107
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer chemistry
|
|---|
| Research Institution | University of Fukui |
|---|
Principal Investigator |
SASAKI Takashi University of Fukui, 大学院・工学研究科, 准教授 (50242582)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,200,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥600,000)
Fiscal Year 2008: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Fiscal Year 2007: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2006: ¥1,600,000 (Direct Cost: ¥1,600,000)
|
|---|
| Keywords | 高分子物性 / ガラス転移 / 高分子構造・物性 / ナノカプセル / 示差走査熱分析 |
|---|
| Research Abstract |
本研究は,厚さが数十ナノメートルの高分子からなるシェル層と,カルシウム結晶体のコア部分で構成されるカプセル微粒子の熱物性,とくにガラス転移温度(T_g)での分子運動特性を明らかにすることを目的とした。高分子シェルのガラス転移挙動はナノサイズのシェルに特有の特異なT_gの上昇や運動の協同性の減少挙動がみられることがわかった。これはコア/シェル界面の影響や高分子網目構造の不均一性などに起因することが示された。
|