Improvement of Cold Working Ability and Strength of Titanium Alloy(Application of Stress-induced Transformation)
| Project/Area Number |
18560080
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Kyoto Institute of Technology |
|---|
Principal Investigator |
MORITA Tatsuro Kyoto Institute of Technology, 工芸科学研究科, 准教授 (90239658)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,710,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥510,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2006: ¥1,500,000 (Direct Cost: ¥1,500,000)
|
|---|
| Keywords | チタン合金 / 熱処理 / 冷間加工性 / 強度 / 応力誘起変態 |
|---|
| Research Abstract |
代表的なα+β型チタン合金であるTi-6Al-4Vに比較的低温で短時間溶体化処理を施すことにより, 応力誘起変態が生じうる残留β相やα"相の体積率を恣意的に上昇させ, 逆に強度上昇をもたらすα'マルテンサイト相の生成量を極力押さえることで冷間加工性が改善された. また, 冷間加工後に短時間時効処理を施すことにより, 元材と同程度の水準まで静的強度の回復が可能であることが明らかとなった. さらに, 短時間2段階熱処理により疲労強度が改善可能であることが示された.
|