| Project/Area Number |
18560083
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | University of the Ryukyus |
|---|
Principal Investigator |
MAKABE Chobin University of the Ryukyus, 工学部, 教授 (70181609)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KONDOU Ryouji 国立大学法人琉球大学, 工学部, 准教授 (80404549)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,010,000 (Direct Cost: ¥2,500,000、Indirect Cost: ¥510,000)
Fiscal Year 2008: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2007: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Fiscal Year 2006: ¥800,000 (Direct Cost: ¥800,000)
|
|---|
| Keywords | 材料設計 / プロセス / 物性 / 評価 / 傾斜材料 / 塑性変形 / 塑性加工 / E-CAP法 / ねじり / 押出し / 材料強度 / 硬さ / 傾斜機能 / 材料強度特性 / 機械材料・材料力学 / 金属物性 / 機械工作・生産工学 |
|---|
| Research Abstract |
塑性加工によって、軽金属等の結晶粒を微細化し強度特性を改善する手法について検討した。本研究手法は、材料をねじり押出すことに大きな特徴があり、特にねじり変形によって加工ひずみに差が生じることに起因して、内部と表面層で異なる性質の素材が形成される。ねじり押出し加工した場合、表面層と内部で硬さの異なる材料が作製され、特にアルミニウムにおいては、静的強度特性および疲労強度特性が共に改善されることがわかった。
|