Study on Surface Fatigue Strength of Machine Elements with Ultra-Fine Crystal Structure by Observations on Macroscopic and Microscopic Scales
| Project/Area Number |
18560135
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | Kagawa University |
|---|
Principal Investigator |
OHUE Yuji Kagawa University, 工学部, 准教授 (60203709)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,020,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥420,000)
Fiscal Year 2008: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2007: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2006: ¥2,200,000 (Direct Cost: ¥2,200,000)
|
|---|
| Keywords | 機械要素 / トライボロジー / 環境材料 / 長寿命化 / 超微細粒鋼 / 面圧疲労強度 / 歯車 / 軸受 / ピッチング |
|---|
| Research Abstract |
結晶を微細化する熱処理とショットピーニングを組み合わせた材料強化加工法によって微細結晶化するメカニズムを調査し, しゅう動機械要素の表面強度向上を実現するための加工条件を明らかにすることを目的としている. 提案加工法では長寿命化が可能で, 加工時間の短縮に由来する製造コスト低減を達成できる. さらに, 加工により創製されるディンプル形状は油膜厚さを向上させる. 提案加工法は, 材料表面特性と潤滑性能の観点から従来の方法よりも有利であった.
|