Basic research of ultrahigh density toribo-memory using nanoperiod multilayer films as storage media
| Project/Area Number |
18560140
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | Nippon Institute of Technology |
|---|
Principal Investigator |
MIYAKE Shojiro Nippon Institute of Technology, 工学部, 教授 (70229813)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,190,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥690,000)
Fiscal Year 2008: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Fiscal Year 2007: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2006: ¥1,200,000 (Direct Cost: ¥1,200,000)
|
|---|
| Keywords | トライボロジー / データストレージ / ナノ材料 / 原子間力顕微鏡 / データストーレージ |
|---|
| Research Abstract |
超高密度記録媒体として物性の異なった層を積層した(Si/C),(C/BN)等のナノ周期積層膜を形成した。ここで(Si/C),(C/BN)膜については1nm 膜厚のナノ周期積層膜を実現した。超高密度記録のためのナノ加工特性の検討として、導電性加工工具(チップ)を用い放電と機械作用を併用した新しい加工を実現した。さらに原子間力顕微鏡(AFM)でダイヤモンドチップを用いて、1 層(1nm)以下の機械加工を実現した。ナノ周期積層膜に加工された情報を再生する方法として、(1)形状差、(2)摩擦力の差、(3)電流分布の差を取り上げ、加工深さに対応する物性の差を評価した。
|
Report
(4 results)
Research Products
(69 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Presentation] 極薄膜DLC のスクラッチ特性2008
Author(s)
押元幸一, 黒坂渡, 松本安哲, 三宅正二郎, 金鍾得
Organizer
トライボロジー会議予稿集 2008-5(pp.101-102)
Place of Presentation
東京
Year and Date
2008-05-15
Related Report
-
-
-
-
[Presentation] 極薄膜DLCのスクラッチ特性2008
Author(s)
押元幸一, 黒坂渡, 松本安哲, 三宅正二郎, 金鍾得
Organizer
日本トライボロジー学会
Place of Presentation
東京, 国立オリンピック記念青少年総合センター
Year and Date
2008-05-15
Related Report
-
-
-
-
-
-
-
-
-
-
-
-
-
-