Development of Lubricative Oxides Coatings
| Project/Area Number |
18560149
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
TOSA Masahiro National Institute for Materials Science, 材料信頼性センター, グループリーダー (20343832)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KASAHARA Akira 独立行政法人物質・材料研究機構, 材料信頼性センター, 主幹研究員 (70354355)
GOTO Masahiro 独立行政法人物質・材料研究機構, 材料信頼性センター, 主幹研究員 (00343872)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,700,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥600,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2006: ¥1,100,000 (Direct Cost: ¥1,100,000)
|
|---|
| Keywords | トライボロジー / コーティング / 固体潤滑剤 / 軌道環境 / 暴露試験 / 真空 / 表面分析 / 摩擦測定 / 固体潤滑材 / トライポロジー |
|---|
| Research Abstract |
TiN他4種類の真空用固体潤滑材料(Cu、MoS2、およびCu+BN)をSUS304系ステンレス鋼基板にスパッタ蒸着被覆した試料について、JAXAと共同で軌道上にて1年間から最長約3年の長期にわたり暴露した後地上に回収した各試料について、摩擦特性、微小硬度、表面構造等を分析して軌道用固体潤滑被覆膜の軌道環境暴露の影響について検討するとともに、各特性変化特に真空中摩擦に原子状酸素照射による酸化が及ぼすメカニズムについて解明することができ、表面酸化改質による潤滑被覆膜の開発技術の基盤を確立することができた。
|