Investigation of single-crystal growth and relationship between magnetoresistance and self-organization in double-perovskite oxides
Project/Area Number |
18560318
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Electronic materials/Electric materials
|
Research Institution | Ibaraki University (2007-2008) Tokyo University of Science, Yamaguchi (2006) |
Principal Investigator |
YOSHIDA Koji Ibaraki University, 大学教育センター, 講師 (80341254)
|
Project Period (FY) |
2006 – 2008
|
Project Status |
Completed (Fiscal Year 2008)
|
Budget Amount *help |
¥2,920,000 (Direct Cost: ¥2,500,000、Indirect Cost: ¥420,000)
Fiscal Year 2008: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2007: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2006: ¥1,100,000 (Direct Cost: ¥1,100,000)
|
Keywords | ダブルペロブスカイト型酸化物 / 単結晶育成 / 巨大磁気抵抗効果 / 構造転移 / 金属-絶縁体転移 / 強磁性転移 / 自己組織化 / 強相関エレクトロニクス / 複合材料・物性 / 巨大磁気抵抗 |
Research Abstract |
FZ法によりダブルペロブスカイト型酸化物A_2FeMoO_6(A=Sr, Ba)の良質・大型単結晶の育成に成功した。一方、MoをFeに置換したSr_2Fe_(1+x)Mo_(1-x)O_6について、多結晶試料を作製し、この物質のドーピング量の変化と物性について詳しく調べた。その結果、x=0.4近傍で、室温での結晶構造が正方晶から立方晶に変化すること、金属から絶縁体に転移すること、強磁性から常磁性に転移することを明らかにした。
|