| Project/Area Number |
18560319
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Electronic materials/Electric materials
|
|---|
| Research Institution | Sojo University |
|---|
Principal Investigator |
MUNAKATA Makoto Sojo University, 情報学部, 教授 (10183112)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
AOKI Shinnichi 崇城大学, 情報学部, 教研 (70175727)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,780,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥480,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2006: ¥1,700,000 (Direct Cost: ¥1,700,000)
|
|---|
| Keywords | 10GHz超 / マイクロ波 / 電磁界収束材料 / 磁性膜 / 誘電体膜 / 集積回路 / ナノ構造磁性膜 / 積層ハイブリッド膜 / マイクロ波電磁界収束材料 / MMICデバイス / 高周波磁気特性 / B添加効果 / 下地層 / ナノ結晶磁性膜 / 結晶向 / 磁区構造 / 磁壁移動 / 伝送線路特性 / ハイブリッド効果 / 軟磁性薄膜 / 磁気共鳴周波数 / 一軸異方性磁界 / ハイブリッド化 / 高飽和磁化 / Ru, Cu下地層 / ナノ結晶 |
|---|
| Research Abstract |
10GHz超のマイクロ波の電磁界を収束する材料の開発を目的として,CoFeBおよびCoFe磁性薄膜を回転電極型スパッター法により試作した.その結果,10GHz超の高周波透磁率特性を有する磁性膜を得,さらにこれを誘電体(ポリイミド膜,SiO2膜)と積層した結果,誘電率特性と透磁率特性のハイブリッド効果すなわち電磁界収束効果が確認された.これによって,マイクロ波集積回路(MMIC)における伝送線路の短縮化,アンテナその他のLC素子の集積化を実現する電磁界束材料の設計・製作が十分に可能であることが明らかにされた.
|