| Project/Area Number |
18560321
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Electronic materials/Electric materials
|
|---|
| Research Institution | Nara National College of Technology |
|---|
Principal Investigator |
FUJITA Naoyuki Nara National College of Technology, 電気工学科, 教授 (90249813)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
NISHINO Satoru 奈良工業高等専門学校, 物質化学工学科, 助教 (20413817)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,970,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥570,000)
Fiscal Year 2008: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2007: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2006: ¥1,500,000 (Direct Cost: ¥1,500,000)
|
|---|
| Keywords | 金属-高分子グラニュラ薄膜 / 金属-高分子同時電析法 / 自己組織化 / ナノ構造 / 金属-高分子コンポジット / 電気化学成膜法 / 電磁波吸収材料 / 電気化学的成膜 / ナノ構造材料 / 磁性材料 / 軟磁性 / 水溶性樹脂 |
|---|
| Research Abstract |
研究成果の概要:有害な電磁波の吸収を行う新素材などとして注目される金属-高分子ナノグラニュラ薄膜を水の中のメッキ反応に類似した方法を使って作製することを試みた.本方法は,従来法に比べ,コストが安い,低温での作製が可能であるなどの特長がある.今回の研究で,金属と絶縁性高分子を含む薄膜の作製に初めて成功し,また,2種類の高分子を混合することによって,その混合割合で膜の構造が変化することを見出すことができた.
|