DEVELOPMENT OF DETECTIVE METHOD FOR DEGRADATION UNDER PAINT FILM USING EXPOSURE SAMPLE
Project/Area Number |
18560471
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Structural engineering/Earthquake engineering/Maintenance management engineering
|
Research Institution | Tokai University |
Principal Investigator |
KAWAKAMI Tetsutaro Tokai University, 海洋学部, 教授 (40204680)
|
Project Period (FY) |
2006 – 2008
|
Project Status |
Completed (Fiscal Year 2008)
|
Budget Amount *help |
¥3,810,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥510,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2006: ¥1,600,000 (Direct Cost: ¥1,600,000)
|
Keywords | 非破壊評価 / 防食塗膜 / 維持管理 / 波動伝播特性 / 維持管理手法 / 暴露サンプル評価 / 低周波振動 / 動的応答特性 / 鋼製海洋構造物 / モニタリング / 暴露サンプル / 劣化評価 / 振動特性 / 防食 / 曝露サンプル |
Research Abstract |
鋼製海洋構造物の塗膜防食された鋼材の劣化を効率的に評価するために,設置された平板暴露サンプルの効率的かつ簡便的劣化評価手法として,低周波波動伝播特性を利用することを考えた.研究成果として,暴露サンプル内の波動の振幅比分布より,劣化部の代表寸法や劣化深さが同定可能であることが明らかとなった.さらに,実験及び数値シュミレーションにより得られた,波動振幅比分布はよく一致しており,理論的及び実験的にも本研究で提案した劣化部検知手法の有用性が確認された.
|