Development of high-performance n-type thermoelectric conversion carbide materials
| Project/Area Number |
18560654
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Nagoya Institute of Technology |
|---|
Principal Investigator |
FUKUDA Koichiro Nagoya Institute of Technology, 工学研究科, 教授 (90189944)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
HASHIMOTO Shinobu 名古屋工業大学, 工学研究科, 准教授 (10242900)
YOSHIDA Hideto 東京大学, 理学研究科, 技術職員 (30376553)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,820,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥420,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2006: ¥2,000,000 (Direct Cost: ¥2,000,000)
|
|---|
| Keywords | 結晶構造 / 組織制御 / 熱電変換材料 / 熱電変換 / 炭化物 / ホモロガス相 / 層状構造 / X線粉末回折 / X線回折 |
|---|
| Research Abstract |
Zr-Al-C系で五種類の新規層状炭化物(ZrAl_4C_4とZr_2Al_4C_5, Zr_3Al_4C_6, ZrAl_8C_7, Zr_2Al_8C_8)を発見した. これらは一般式(ZrC)_l(Al_4C_3)_m(l=1~3, m=1~2)の新規ホモロガス相に属し, n型熱電変換材料として高い性能指数を示した. Zr席にYを, Al席にSiとGeを固溶置換すると熱電特性が操作できた. 理論計算の結果も熱電材料としての有望性を示した.
|