| Project/Area Number |
18560684
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Structural/Functional materials
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
SHINOHARA Yoshikazu National Institute for Materials Science, 材料ラボ, グループリーダー (70343853)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
IMAI Yoshio 独立行政法人物質・材料研究機構, 材料ラボ, 主幹研究員 (40354138)
ISODA Yukihiro 独立行政法人物質・材料研究機構, 材料ラボ, 主任研究員 (80354140)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,550,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥450,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2006: ¥1,600,000 (Direct Cost: ¥1,600,000)
|
|---|
| Keywords | 熱・エネルギー材料 / 熱電エネルギー変換 / 高分子 / 熱電特性 / ポリチオフェン / 有機合成 / ゼーベック係数 / 導電率 |
|---|
| Research Abstract |
ポリチオフェン系導電性高分子の電気伝導は主鎖分子間伝導が支配的でることを明らかにした。高い熱電特性を有するポリチオフェン系材料を開発するためには、1)主鎖間隔を制御して室温以上の温度域でも最近接間ホッピングを実現すること、2)主鎖分子配向によって単位体積当たりの主鎖密度を高めて高い導電率を実現すること、が必要となる。主鎖分子の配列・配向制御がポリマー系熱電材料実現の鍵になると言える。
|