Preparation of electorolessly deposited cobalt alloy films with amorphous-nano modulated structures
| Project/Area Number |
18560699
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | University of Hyogo |
|---|
Principal Investigator |
HITOSHI Matsuda University of Hyogo, 大学院・工学研究科, 教授 (60118015)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YAE Shinji 兵庫県立大学, 大学院・工学研究科, 准教授 (00239716)
FUKUMURO Naoki 兵庫県立大学, 大学院・工学研究科, 助教 (10347528)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,100,000 (Direct Cost: ¥2,800,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2007: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2006: ¥1,800,000 (Direct Cost: ¥1,800,000)
|
|---|
| Keywords | 無電解めっき / アモルファス / ナノ結晶 / 変調構造 / 傾斜構造膜 / 磁気履歴曲線 / 保磁力 / 磁化履歴曲線 |
|---|
| Research Abstract |
物質は、原子が規則正しく配列する「結晶質」と配列がランダムな「アモルファス」に分類できる。無電解めっき法で作製条件によって、アモルファスから結晶質まで種々の膜を形成可能である。この研究では、(1) 1枚の膜の中で、結晶がアモルファスから結晶質へ少しずつ変化する構造傾斜膜(2) 1枚の膜の中でアモルファスと結晶質が幾何学的に配列した2相変調構造膜の作製に成功した。また、その構造観察や磁気特性解析を行い、実用化の基礎資料を提示した
|