Hybrid nanofractography of ceramics
| Project/Area Number |
18686053
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (A)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Yokohama National University |
|---|
Principal Investigator |
TATAMI Junichi Yokohama National University, 大学院・環境情報研究院, 准教授 (30303085)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥30,420,000 (Direct Cost: ¥23,400,000、Indirect Cost: ¥7,020,000)
Fiscal Year 2008: ¥5,330,000 (Direct Cost: ¥4,100,000、Indirect Cost: ¥1,230,000)
Fiscal Year 2007: ¥5,330,000 (Direct Cost: ¥4,100,000、Indirect Cost: ¥1,230,000)
Fiscal Year 2006: ¥19,760,000 (Direct Cost: ¥15,200,000、Indirect Cost: ¥4,560,000)
|
|---|
| Keywords | セラミックス / 破壊 / 強誘電体 / 圧電体 / 磁性体 / 走査型プローブ顕微鏡 / 磁気力顕微鏡 / 走査型非誘電率顕微鏡 / 非線形誘電率顕微鏡 / チタン酸バリウム / PZT |
|---|
| Research Abstract |
チタン酸バリウムやフェライトなどの機能性セラミックスのき裂および破面を走査型プローブ顕微鏡で観察し、ナノスケールでの破壊形態の三次元的評価と表面近傍の物性の同時測定による破壊挙動の解析(ハイブリッドナノフラクトグラフイー)を行った。これらの材料には電気的あるいは磁気的分極の異なる領域からなるドメインが存在することが知られていたが、本研究のハイブリッドナノフラクトグラフィーにより、機能性セラミックスのき裂先端近傍および破面にはき裂先端の特異応力場に起因して通常のバルク体とは異なるドメイン構造があらわれることをはじめて明らかにした。
|