Deposition of vapor-grown cone-shaped graphitic whiskers in the cavities of wood cells ;functioning of wood cell as microreactor
| Project/Area Number |
18688008
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (A)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
林産科学・木質工学
|
|---|
| Research Institution | The University of Tokyo |
|---|
Principal Investigator |
SAITO Yukie The University of Tokyo, 大学院・農学生命科学研究科, 准教授 (30301120)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥16,120,000 (Direct Cost: ¥12,400,000、Indirect Cost: ¥3,720,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2006: ¥14,040,000 (Direct Cost: ¥10,800,000、Indirect Cost: ¥3,240,000)
|
|---|
| Keywords | 化学加工 / カーボン材料 |
|---|
| Research Abstract |
従来の木材炭化では蒸発してしまっていた熱分解ガスを利用し、炭化を気相で行うことで、これまでにない高い構造規則性を持つ針状炭素物質「円錐黒鉛ウイスカ」を、木材から創り出した。気相炭化法では木材の細胞が(1)原料となる炭素ガスの発生源、(2)炭素ガスを蓄え過飽和状態にして析出させるための反応容器(ある種のマイクロリアクタ)として、二重の役割を担う。2500℃での加熱過程で、細胞壁から発生する熱分解ガス中の炭素を原料として生成した、直径数μm、長さ数十μmの炭素物質「円錐黒鉛ウイスカ」は、ベータ炭化ケイ素結晶が鋳型として、円錐形の炭素六角網面として高度な規則性を持って析出する。このユニークな構造規則に由来する、磁場配向性、複屈折性、ウイスカ表面のカーボンナノチューブを巻きつけたような構造(Nanoterminated surface structure; NTSS)が明らかとなった。
|