Chemical design of water-soluble titanium complec and phase and morphology control of titanium-based oxide materials by wide-ranges hydrothermal process
| Project/Area Number |
18750177
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Tokai University |
|---|
Principal Investigator |
TOMITA Koji Tokai University, 理学部, 講師 (00419235)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,780,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥180,000)
Fiscal Year 2008: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2007: ¥1,700,000 (Direct Cost: ¥1,700,000)
Fiscal Year 2006: ¥1,300,000 (Direct Cost: ¥1,300,000)
|
|---|
| Keywords | 水溶性チタン錯体 / チタン系酸化物材料 / 広角的水熱プロセス / ナノ粒子 / 形態制御 / 水熱プロセス / 光触媒 / 酸化チタン / 多形 / 蛍光体 |
|---|
| Research Abstract |
水溶性チタン錯体を酸性・中性・塩基性の広い条件化で水熱処理することで種々の酸化チタンを合成することに成功した。水溶性チタン錯体の一つであるグリコール酸チタン錯体を原料に用いることで、アナターゼ型、ルチル型、ブルカイト型、B型の4種類の結晶構造を作り分けることに成功した。また、酒石酸チタン錯体を原料とすることで、ルチル型酸化チタンのナノ粒子やアナターゼ型酸化チタンのニードル状微粒子など、特異な形状を持った試料の作製にも成功した。
|