| Project/Area Number |
18K12569
|
|---|
| Research Category |
Grant-in-Aid for Early-Career Scientists
|
| Allocation Type | Multi-year Fund |
|---|
| Review Section |
Basic Section 03060:Cultural assets study-related
|
|---|
| Research Institution | Tokyo National Museum (2020-2023)
The Kyoto Costume Institute (2018-2019) |
|---|
Principal Investigator |
佐藤 萌 独立行政法人国立文化財機構東京国立博物館, 学芸研究部, 研究員 (20801632)
|
|---|
| Project Period (FY) |
2018-04-01 – 2026-03-31
|
| Project Status |
Granted (Fiscal Year 2023)
|
| Budget Amount *help |
¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000)
Fiscal Year 2021: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2020: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2019: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2018: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
|
|---|
| Keywords | 染織文化財 / 保存修復 / タンニン酸 / 鉄媒染 / 劣化 |
|---|
| Outline of Annual Research Achievements |
天然染料のタンニン酸と鉄媒染で染色された黒染め染織文化財の劣化が、作品を収蔵する世界中の美術館や博物館で深刻な問題となっている。その原因は、繊維中の過剰な二価鉄イオンが空気中の酸素と反応して過酸化水素とヒドロキシラジカルが生成されることで、酸化触媒作用や酸触媒作用が進行することによると考えられている。しかし未だ有効な実践的処置法の開発にまでに至らないのが現状である。本研究では、脱酸性化・抗酸化・強化処置の役割を持つ単体の処置剤または最適な組み合わせの処置剤を用いて、黒染め染織文化財保存修復のための実践的研究を行うことを目的とする。モデル布帛には絹と綿を使用し、浴比50倍量の1 wt%タンニン酸水溶液で60分間70℃にて染色した後、浴比50倍量の2 wt%硫酸第一鉄水溶液で30分間40℃にて媒染する工程を3回繰り返した。80℃、65%RH雰囲気下で絹布帛は2-4週間、綿布帛は1-3日間を加速劣化の条件とした。0.2, 0.6, 1.4 wt%フノリ水溶液、1 wt%膠水溶液を処置剤として使用し、加速劣化前後でモデル布帛に塗布して、処置剤の劣化抑制効果を検討した。評価方法については、分光測色計で色の変化を調べ、pH測定により酸性度を調べ、バソフェナントロリン試験（二価鉄指示薬紙）により処置後の二価鉄イオンを定性し、引張試験機により物性試験を行った。フノリと膠による各処置により、酸性度の軽減、二価の遊離鉄イオン量の低下、引張強度保持の効果が確認された。
|
| Current Status of Research Progress |
Current Status of Research Progress
4: Progress in research has been delayed.
Reason
研究中断をしていた期間があることによる。
|
| Strategy for Future Research Activity |
引き続きフノリと膠の濃度および塗布方法の調整を行い、劣化抑制効果の有無を検証する。文献調査により脱酸化・抗酸化・強化処置剤の検討を継続する。スプレー・刷毛・ローラー・ネブライザーなど実際に染織品保存修復の現場で用いられる塗布方法により、処置の効果を検証する。研究結果を解析・検証し、論文や学会発表の準備をする。
|