Surface-Induced Chemical Liquid Deposition of Schiff Base Type p-Conjugated Polymers
| Project/Area Number |
19310075
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nanomaterials/Nanobioscience
|
|---|
| Research Institution | Kumamoto University |
|---|
Principal Investigator |
KUNITAKE Masashi Kumamoto University, 大学院・自然科学研究科, 教授 (40205109)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
杉本 学 熊本大学, 大学院・自然科学研究科, 准教授 (80284735)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
SUGIMOTO Manabu 熊本大学, 大学院・自然科学研究科, 准教授 (80284735)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥19,760,000 (Direct Cost: ¥15,200,000、Indirect Cost: ¥4,560,000)
Fiscal Year 2008: ¥6,240,000 (Direct Cost: ¥4,800,000、Indirect Cost: ¥1,440,000)
Fiscal Year 2007: ¥13,520,000 (Direct Cost: ¥10,400,000、Indirect Cost: ¥3,120,000)
|
|---|
| Keywords | ナノ材料創成 / ナノ表面界面 / π共役高分子 / 超薄膜 / 化学液相成長 |
|---|
| Research Abstract |
pHにより反応を制御することで、固液または液液界面に選択的にシフベースで結合されたπ共役高分子薄膜を成長させる化学液相成長法を考案し、検討した。溶液相では、ギリギリ反応が進行しない条件に設定しておくと、疎水性基板上において選択的に表面で反応が進行することを見いだした。単分子膜レベルでは、π共役高分子鎖の一次元配列や、ポルフィリンを用いた二次元π共役高分子の形成と観察に成功した。さらに多層化条件では、ナノシート構造やバンドル構造をもつ薄膜の作成に成功した。
|
Report
(3 results)
Research Products
(19 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Presentation]2007
Author(s)
樋口 倫太郎(代表者)
Organizer
高分子討論会
Place of Presentation
名古屋工業大学
Year and Date
2007-09-20
Related Report
-
-
-
-