Study on High-Strength and Electronic Materials with Carbon Nanotube and Polymer composite using Dielectrophoresis
Project/Area Number |
19310081
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Nanomaterials/Nanobioscience
|
Research Institution | National Institute for Materials Science |
Principal Investigator |
TANG Jie National Institute for Materials Science, 材料信頼性萌芽ラボ, グループリーダー (80354158)
|
Co-Investigator(Kenkyū-buntansha) |
SASAKI Taizo 独立行政法人物質・材料研究機構, 計算科学センター, グループリーダー (60343852)
ZHANG Han 独立行政法人物質・材料研究機構, 材料ラボ, NIMSポスドク研究員
|
Project Period (FY) |
2007 – 2009
|
Project Status |
Completed (Fiscal Year 2009)
|
Budget Amount *help |
¥17,290,000 (Direct Cost: ¥13,300,000、Indirect Cost: ¥3,990,000)
Fiscal Year 2009: ¥5,590,000 (Direct Cost: ¥4,300,000、Indirect Cost: ¥1,290,000)
Fiscal Year 2008: ¥5,590,000 (Direct Cost: ¥4,300,000、Indirect Cost: ¥1,290,000)
Fiscal Year 2007: ¥6,110,000 (Direct Cost: ¥4,700,000、Indirect Cost: ¥1,410,000)
|
Keywords | カーボンナノチューブ / 導電ポリマー / 複合材料 / エレクトロニクス材料 / 高強度材料 |
Research Abstract |
Continuous long carbon nanotube fibers with good mechanical stiffness and strength are highly desirable for use in composite materials. We have established a reliable and high throughput dielectrophoretic method to fabricate carbon nanotube fribils at room temperature. It is very promising that these highly conductive fibrils will have wide applications as conductive composite, especially in integrated circuits and biological, energy application areas.
|