Ionic electrode for fast oxide ion conductor based on bismuth related oxides
| Project/Area Number |
19360344
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making engineering
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
AWAKURA Yasuhiro Kyoto University, 大学院・工学研究科, 教授 (70109015)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
UDA Tetsuya 京都大学, 大学院・工学研究科, 准教授 (80312651)
KOYAMA Yukinori 京都大学, 大学院・工学研究科, 助教 (20437247)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥20,930,000 (Direct Cost: ¥16,100,000、Indirect Cost: ¥4,830,000)
Fiscal Year 2008: ¥4,940,000 (Direct Cost: ¥3,800,000、Indirect Cost: ¥1,140,000)
Fiscal Year 2007: ¥15,990,000 (Direct Cost: ¥12,300,000、Indirect Cost: ¥3,690,000)
|
|---|
| Keywords | ビスマス酸化物 / 固体電解質 / 酸素ポンプ / 熱力学 / 電気化学 |
|---|
| Research Abstract |
ビスマスーバナジウム系複合酸化物(Bi_2VO_<5.5>およびV サイトを一部置換したBi_2V_<1-x>TaxO_<5.5>など)は500℃程度の中温域で高い酸化物イオン伝導性を示す物質であり、固体電解質を用いた酸素濃縮器などへの応用が期待される。本研究ではBi_2VO_<5.5>系電解質に適した電極触媒層を探索した。具体的には、電解質の表面のみをイオン交換法により銅置換することを試み、電極触媒層の形成に試みた。次に電極触媒層として、貴金属サーメットの利用が可能であるかの検証を試みた。結果、Bi_2V_<0.8T>a_<0.2>O_<5.5>はPtとは反応せず、PdやAgとは反応することが分かった。
|