Synthesis of Mordenite Nanocrystals and its Application to Structured Catalytic Reactor for Complicated Reactions
| Project/Area Number |
19360356
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Reaction engineering/Process system
|
|---|
| Research Institution | Hokkaido University |
|---|
Principal Investigator |
MASUDA Takao Hokkaido University, 大学院工学研究科, 教授 (20165715)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TAGO Teruoki 北海道大学, 大学院・工学研究科, 准教授 (20304743)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000)
Fiscal Year 2008: ¥7,540,000 (Direct Cost: ¥5,800,000、Indirect Cost: ¥1,740,000)
Fiscal Year 2007: ¥11,050,000 (Direct Cost: ¥8,500,000、Indirect Cost: ¥2,550,000)
|
|---|
| Keywords | 反応装置 / 構造体触媒反応器 / 触媒膜 / ゼオライトナノクリスタル / モルデナイト / 界面活性剤 / アルキル化反応 / ナフタレン / ナノサイズゼオライト / 構造体触媒 / 構造性活性点 / ジメチルナフタレン / 分子篩 |
|---|
| Research Abstract |
水/界面活性剤/有機溶媒を利用するゼオライト合成法により, モルデナイト結晶のナノサイズ化に成功した. ナノサイズモルデナイト結晶の外表面酸点を, 有機シラン化合物由来シリカにより選択的に不活性化させた構造性活性点を有する触媒の開発, およびモルデナイトナノクリスタルを積層させた膜型構造体触媒反応器の開発に成功した. 同モルデナイト触媒はナフタレンからの2,6-ジメチルナフタレン選択合成に高活性を示した.
|