Development of Lead-Free Copper Alloy Based on Life Cycle Assessment
| Project/Area Number |
19510101
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Environmental technology/Environmental materials
|
|---|
| Research Institution | Kagoshima University |
|---|
Principal Investigator |
SUEYOSHI Hidekazu Kagoshima University, 大学院・理工学研究科, 教授 (70041548)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MAEDA Yoshikazu 鹿児島大学, 工学部, 技術専門職員 (80448563)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2008: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Fiscal Year 2007: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
|
|---|
| Keywords | 鉛フリー銅合金 / 硫化銅 / ライフサイクルアセスメント / エコマテリアル / 被削性 / 機械的性質 / インベントリ分析 / 地球温暖化 / 酸性化 / エネルギー資源の消費 / 金属資源の消費 / 二硫化モリブデン / 引張特性 |
|---|
| Research Abstract |
これまでに開発された鉛フリー銅合金には、被削性向上の目的でビスマス、セレン等の特殊元素が添加されている。しかし、これらの希少元素の使用はLCAの観点からは好ましくない。本研究では、硫化銅を分散させた新しい鉛フリー銅合金を開発した。この合金は従来の鉛フリー銅合金に匹敵する被削性と機械的性質を有すること、LCA解析の結果、この合金の生産システムへの移行によって、地球環境への負荷は低減することが明らかになった。
|